Short answer: Graphitization is a form of selective leaching in carbon and low-alloy steel and cast iron — long service at high temperature causes carbon to precipitate as graphite, leaving a soft, weak, brittle remnant. Avoid it by using low-carbon or alloy steels and by controlling weld heat and service temperature.
At a Glance
Where It Happens
Graphitization is a selective-leaching failure like Metal Selective Leaching Guide; estimate loss with Metal Corrosion Rate Calculation Guide and monitor via Metal Corrosion Monitoring Guide. Study structure with Metal Metallography Guide.
Prevent & Inspect
Use low-carbon or alloy grades and control weld HAZ; inspect by Metal Ndt Guide and document per Mill Test Certificate Guide. Protect stock via How To Prevent Metal Rust.
QA & Supply
HXSCO supplies low-carbon and alloy grades selected to resist graphitization.
Get a Quote
Tell HXSCO your requirements and we will respond with a competitive quote and lead time.
Häufig gestellte Fragen
Carbon precipitating as graphite in steel/cast iron, weakening it.
Long high-temperature service, especially in welds and cast iron.
Yes — both are selective leaching that leaves a weak remnant.
Use low-carbon or alloy steel and limit high-temperature exposure.
HXSCO supplies low-carbon and alloy grades for high-temperature service.
Source Graphitization-Resistant Steel from HXSCO
HXSCO supplies low-carbon and alloy steel grades selected to resist graphitization in high-temperature service. Send your spec and quantity for a quote.